EFFECTS OF SOL-GEL PROCESSING FACTORS ON TRANSMITTANCE AND SURFACE FREE ENERGY OF TEOS-SIO2-PDMS FILMS
Keywords:
Transmittance, surface free energy, statistical analysisAbstract
Hydrophobic film coatings on ceramic surfaces have been widely studied for decades. Many hydrophobic films have been synthesized but only a few of them have high transmittance and low surface energy. This research investigated the sol-gel processing factors that affect the transmittance and surface free energy of hydrophobic films. In this study, films were made of TEOS (tetraethyl orthosilicate), nano-particle size silica and PDMS (poly-dimethylsiloxane). The amount of silica (0.5, 5, and 10 wt%), the size of the silica (12 and 20 nm), and the heat treatment temperature (300 and 400oC were varied as independent factors. Transmittance and surface free energy were observed to be dependent factors. Design-Expert® software was used to design and analyze the experiments. The results showed that the transmittance and surface free energy decreased significantly as the amount of silica was increased.The lowest transmittance value (62%) and surface free energy (3 mN/m) were observed when using a silica size of 20 nm at 10wt%with heat treatment at 300oC. The highest value of the transmittance (90%) was obtained when using a silica size of 12 or 20 nm at 0.5wt%and heat treatment at 300oC.
References
DataPhysics Instruments GmbH. (2013). Introduction into methods of measuring andanalyzingcontact angles for the determination of surface free energies ofsolids. Filderstadt.:DataPhysics. Available from: www.dpc.kt.dtu.dk/upload/ centre/dpc/documents/instrumentation/dataphysics-measuring%20cas.pdf. Accessed date: Jan 8, 2013.
Huang, Y.Y. and Chou, K.S. (2003).Studies on the spin coating process of silicafilms. Ceram. Int., 29:485.
Hwang, J.H., Lee, B.I., Klep, V., and Luzinov, I. (2008). Transparent hydrophobicorganic-inorganic nanocomposite films. Mater. Res. Bull., 43(10):2652.
Jones, A., Lamb, R.N., and Zhang, H., inventors; Unisearch Limited, Assignee. June 1, 2004. Hydrophobic Material. U.S. patent no. 6,743,467 B1.
Kamitani, K. and Teranishi, T. (2003). Development of water-repellent glassimproved water-sliding property and durability. J. Sol-Gel Sci. Techn., 26:823.
Ma, M. and Hill, R.M. (2006). Superhydrophobic surfaces. Curr. Opin. Colloid Int., 11;193.
Nadargi, D.Y., Gurav, J.L., El Hawi, N., Rao, A.V., and Koebel, M. (2010). Synthesis and characterization of transparent hydrophobic silica thin films bysingle step sol–gel process and dip coating. J. Alloy.Compd., 496(1-2):436.
Nakajima, A., Abe, K., Hashimoto, K., and Watanabe, T. (2000). Preparation of hardsuper-hydrophobic films with visible light transmission. Thin Solid Films, 376:140.
Nakajima, A., Hashimoto, K., and Watanabe, T. (2001). Recent studies on super-hydrophobic films. Monatsh.Chemie., 132:31.
Nimittrakoolchai, O. and Sitthisuntorn, S. (2010). Deposition of transparent,hydrophobic polydimethylsiloxane-nanocrystalline TiO2 hybrid films on glasssubstrate. Songklanakarin Journal Science Technology, 32:157.
Shindou, T., Katayama, S., Yamada, N., and Kamiya, K. (2004). Effect ofcomposition on surface properties of polydimethylsiloxane-basedinorganic/organic hybrid films. J. Sol-Gel Sci. Techn., 30:229.
Wu, L.Y.L., Tan, G.H., Qian, M., and Li, T.H. (2005). Formulation of transparenthydrophobic sol-gel hard coatings. SIMTech technical reports, 6(2):1.
Zheng, J., Song, J., Jiang, Q., and Lian, J. (2012). Superhydrophobic behavior andoptical properties of ZnO film fabricated by hydrothermal method. J. Mater. Sci. Technol., 28(2):103.